Aluminium production and refinement

Although aluminium is the most abundant metallic element in the Earth's crust (believed to be 7.5 to 8.1 percent), it is rare in its free form, occurring in oxygen-deficient environments such as volcanic mud, and it was once considered a precious metal more valuable than gold. Napoleon III, emperor of France, is reputed to have given a banquet where the most honoured guests were given aluminium utensils, while the other guests had to make do with gold.[9][10] The Washington Monument was completed, with the 100 ounce (2.8 kg) aluminium capstone being put in place on December 6, 1884, in an elaborate dedication ceremony. It was the largest single piece of aluminium cast at the time. At that time, aluminium was more expensive than silver, gold, or platinum. Aluminium has been produced in commercial quantities for just over 100 years.

Aluminium is a strongly reactive metal that forms a high-energy chemical bond with oxygen. Compared to most other metals, it is difficult to extract from ore, such as bauxite, due to the energy required to reduce aluminium oxide (Al2O3). For example, direct reduction with carbon, as is used to produce iron, is not chemically possible, since aluminium is a stronger reducing agent than carbon. Aluminium oxide has a melting point of about 2,000 °C. Therefore, it must be extracted by electrolysis. In this process, the aluminium oxide is dissolved in molten cryolite and then reduced to the pure metal. The operational temperature of the reduction cells is around 950 to 980 °C. Cryolite is found as a mineral in Greenland, but in industrial use it has been replaced by a synthetic substance. Cryolite is a chemical compound of aluminium, sodium, and calcium fluorides: (Na3AlF6). The aluminium oxide (a white powder) is obtained by refining bauxite in the Bayer process of Karl Bayer. (Previously, the Deville process was the predominant refining technology.)

The electrolytic process replaced the Wöhler process, which involved the reduction of anhydrous aluminium chloride with potassium. Both of the electrodes used in the electrolysis of aluminium oxide are carbon. Once the ore is in the molten state, its ions are free to move around. The reaction at the cathode (negative electrode) is

Al3+ + 3 e− → Al
Here the aluminium ion is being reduced (electrons are added). The aluminium metal then sinks to the bottom and is tapped off.

At the anode (positive electrode), oxygen is formed:

2 O2− → O2 + 4 e−
This carbon anode is then oxidized by the oxygen, releasing carbon dioxide.

O2 + C → CO2
The anodes in a reduction cell must therefore be replaced regularly, since they are consumed in the process.

Unlike the anodes, the cathodes are not oxidized because there is no oxygen present, as the carbon cathodes are protected by the liquid aluminium inside the cells. Nevertheless, cathodes do erode, mainly due to electrochemical processes. After five to ten years, depending on the current used in the electrolysis, a cell has to be rebuilt because of cathode wear.


World production trend of aluminiumAluminium electrolysis with the Hall-Héroult process consumes a lot of energy, but alternative processes were always found to be less viable economically and/or ecologically. The worldwide average specific energy consumption is approximately 15±0.5 kilowatt-hours per kilogram of aluminium produced (52 to 56 MJ/kg). The most modern smelters achieve approximately 12.8 kW·h/kg (46.1 MJ/kg). (Compare this to the heat of reaction, 31 MJ/kg, and the Gibbs free energy of reaction, 29 MJ/kg.) Reduction line currents for older technologies are typically 100 to 200 kA; state-of-the-art smelters[11] operate at about 350 kA. Trials have been reported with 500 kA cells.

Recovery of the metal via recycling has become an important facet of the aluminium industry. Recycling involves melting the scrap, a process that requires only five percent of the energy used to produce aluminium from ore. However, a significant part (up to 15% of input material) is lost as dross (ash-like oxide).[12] Recycling was a low-profile activity until the late 1960s, when the growing use of aluminium beverage cans brought it to the public consciousness.

Electric power represents about 20% to 40% of the cost of producing aluminium, depending on the location of the smelter. Smelters tend to be situated where electric power is both plentiful and inexpensive, such as South Africa, the South Island of New Zealand, Australia, the People's Republic of China, the Middle East, Russia, Quebec and British Columbia in Canada, and Iceland.


Aluminium output in 2005In 2005, the People's Republic of China was the top producer of aluminium with almost one-fifth world share, followed by Russia, Canada, and USA, reports the British Geological Survey.

Over the last 50 years, Australia has become a major producer of bauxite ore and a major producer and exporter of alumina.[13] Australia produced 62 million tonnes of bauxite in 2005. The Australian deposits have some refining problems, some being high in silica but have the advantage of being shallow and relatively easy to mine.[14